Yüksek Yoğunluklu Kalsiyum Silikat Blok

Teknik Özellik (Tip-I 650°C)

Kalem

Birim

TUNGKIN-

200

TUNGKIN-

220

JIS A-9510

No.2-22

ASTM C-533

İ harfini yaz

TUNGKIN-

170

JIS A-9510

2-17

Yoğunluk

Kg/m3

<=200

<=220

<=220

<=240

<=170

<=170

Hizmet

Sıcaklık

°C

(°F)

<=650

(<=1200)

<=650

(<=1200)

<=650

<=649

(<=1200)

<=650

(<=1200)

<=650

sıkıştırıcı

Kuvvet

mpa

(kgf/cm2)

>=0.55

(>=5.61)

>=0.58

(>=5.92)

>=0.414

>=0.51

(>=5.20)

termal

İletkenlik

w/mk

(70±5°C)

<=0.060

<=0.062

<=0.062

<=0.065

<=0.054

<=0.055

Nem

%

<=5

<=5

<=5

Doğrusal Büzülme

(650°C 16h)

%

<=2.0

<=2.0

<=2.0

<=2.0

<=2.0

<=2.0

bükme

Kuvvet

mpa

(kgf/cm2)

>=0.42

(>=4.28)

>=0.43

(>=4.38)

>=0.3

(>=3.1)

>=0.310

>=0.41

(>=4.18)

>=0.2

(>=2.0)

Standart boy

Genişlik

304 mm, 305 mm,

Uzunluk

915 mm

Kalınlık

25mm 30mm 40mm 50mm 60mm 65mm 70mm 75mm 80mm 90mm